Effect of finishing and polishing techniques on the surface roughness of a nanoparticle composite resin

To evaluate the surface roughness of the resin Filtek Z350 (3M ESPE) after different finishing and polishing techniques. Methods: Sixty specimens of 7x2 mm were made and distributed in 6 groups (n=10), according to the technique employed: G1 (control) – polyester strip – no finishing or polishing; G2- multi-blade burs; G3- diamond burs 3195F and 3195FF; G4- Diamond ProDiscs (FGM); G5- Sof-Lex Discs (3M ESPE); G6- Robinson bristle brushes with pumice paste for20 s and felt disc with 2-4 ìm diamond paste for 30 s. The specimens were stored in artificial saliva at 37°C for 7 days. After the finishing and polishing techniques, surface roughness (Ra, ìm) was measured using Surf-Corder profilometer SE 1700. Data were subjected to one-way ANOVA andTukey’s test at 5% significance level. Results: G3 presented the highest surface roughness meanvalue (0.61). G5 presented the lowest surface roughness mean value (0.15), but it was not significantly different from G1, G4 and G6. Conclusions: According to the obtained results, Z350 composite resin presented the lowest surface roughness when finishing and polishing systems were used (Sof-lex and Diamond Pro discs and Robinson bristle brush with pumice plus Diamond®felt disc with Diamond Excel® paste). The use of diamond burs (G3) resulted in the highest composite surface roughness. There was no significantly different between G1, G4, G5 and G6.

Rugosidade produzida em restauradores resinosos pela escovaçäo mecânica com escovas dentais complexas / Produced roughness on resin filling by mechanical brushing with complex tooth brushes

Este trabalho avaliou a rugosidade superficial dos restauradores Z100 e Compoglass produzida pela escovaçäo com as escovas dentais Oral-B 30, Alcance Reach Control, Kolinos Doctor Flexível e Colgate Total. Cada grupo de escova foi dividido em dois subgrupos, conforme associaçäo com água e dentifrício. Os corpos-de-prova foram escovadas mecanicamente, e a superfície foi analisada com auxílio de um rugosímetro. O Compoglass escovado com dentifrício e escova Oral-B 30 apresentou a maior média numérica de rugosidade, seguida por Alcance Reach Control e Holynos Doctor Flexível, que näo diferiram entre si estatisticamente, e Colgate Total, com a menor média estatística. Para Z100, näo houve diferença entre a rugosidade produzida após escovaçäo com dentifrício e os diferentes tipos de escovas dentais. O mesmo näo aconteceu com o Compoglass, que também apresentou maior valor de rugosidade superficial em relaçäo ao Z100